Type 201 stainless steel is an austenitic chromium-nickel-manganese stainless alloy. It was developed mid century to conserve nickel and it is used as an alternative to type 301 in some tempered applications. Because of 201 's relatively high yield strength in the annealed condition, use of 201 is limited. Type 201 is generally used in the tempered condition particularly for springs and fasteners. 201 Stainless will retain a comparable ductility to 301 even with the higher yield strength.
Chemistry TypicalCarbon: 0.15 max Manganese: 5.50- 7 .50 max Phosphorus: 0.060 max Sulfur: 0.030 max Silicon: 0.75 max Chromium: 18.00- 20.00 max Nickel: 3.50- 5.50 TEMPERED 1/16 HARD Ultimate Tensile Strength: 95 KSI min (655 MPA min) Yield Strength (0.2% Offset): 45 KSI min (310 MPA min) Elongation: 40% min Tempered 1/8 Hard Ultimate Tensile Strength: 100 KSI min (690 MPA min) Yield Strength (0.2% Offset): 55 KSI min (380 MPA min) Elongation: 45% minTEMPERED 1/4 HARD Ultimate Tensile Strength: 125 KSI min (860 MPA min) Yield Strength (0.2% Offset): 75 KSI min (515 MPA min) Elongation: 25% min
Thickness Range: .0003″ – .188″ (0.0075mm – 4.7752mm)
Springs, Fasteners, Utensils, Appliances, Automotive Trim, Clamps